ITEM: XGT02585-ZR-M-AS（0.25MM*1450MM）
| TEST ITEM | TEST METHOD | UNIT | TEST VALUE |
|---|---|---|---|
| Hardness | ISO 686 | shoreA | 85±2 |
| Specific Gravity | ISO 2781 | g/gm³ | 1.14±0.02 |
| Surface Resistivity | ASTM D-257 | Ohm/square | 1010 |
| Volume Resistivity | ASTM D-257 | Ohm-cm | / |
| Static Decay Rate | FTMS-101C(12% RH) | seconds | / |
| Tensile Strength | ISO 527-3/5/500 | MPa |
CD: 49.1 MD: 48.1 |
| Tensile Strength @ 50% Elongation | ISO 527-3/5/500 | MPa |
CD: 8.49 MD: 7.69 |
| Tensile Strength @ Elongation | ISO 527-3/5/500 | MPa |
CD: 12.68 MD: 11.32 |
| Tensile Strength @ 300% Elongation | ISO 527-3/5/500 | MPa |
CD: 51.23 MD: 48.57 |
| Elongation at Break | ISO 527-3/5/500 | % |
CD: 312.239 MD: 307.386 |
| Tear Strength | ISO 34-1B | kN/m |
CD: 118.47 MD: 110.85 |
| Abrasion Resistance | ISO 4649 | mm³ | 0.36 |
| Vicat Softening Point A50 | ISO 306 | ℃ | 97℃ |
| Melting Point | Kofler | ℃ | 165 |
| Brittle Point | DSC | ℃ | -50℃ |
Anti-Static CLEAR TPU FILM/ Flexible TPU Film/ Surface resistivty is 10^8-10^10